Printed circuit board and method for manufacturing printed circuit board

ABSTRACT

An insulating layer made of an insulator film or the like is prepared. Then, a thin metal film and a thin copper film are formed in sequence on the insulating layer. The thin copper film is subsequently laminated with a dry film or the like, and exposed and developed to form a plating resist thereon that have patterns opposite to conductor patterns which are formed in a subsequent step. This is followed by forming conductor patterns made of copper, by electrolytic plating using an electrolytic copper sulfate plating solution, on the surfaces of the thin copper film where the plating resist is not formed. The plating resist is then removed by, for example, stripping. After this, the thin copper film is held at a temperature of not less than 200° C. and not more than 300° C. for approximately an hour to be thermally treated. Then, the thin copper film and the thin metal film are removed by chemical etching except the portions under the conductor patterns.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to printed circuit boards and a method formanufacturing such printed circuit boards.

2. Description of the Background Art

Printed circuit boards such as flexible printed circuit boards arewidely used in a variety of electrical and electronic devices. A printedcircuit board includes, for example, an insulating layer of, e.g.,polyimide, having on one side or both sides thereof conductor layers of,e.g., a copper foil with prescribed patterns.

Conventionally, conductor layers having prescribed patterns in printedcircuit boards such as flexible printed circuit boards are formed by theknown methods such as the semi-additive, substractive, and full-additivemethods (refer to JP 2002-176259, for example).

The above-mentioned semi additive method is now described with referenceto the drawings.

FIGS. 4 (a), 4 (b), 4 (c), 4 (d), 4 (e), and 4 (f) are schematic crosssectional views showing the steps of a method for manufacturing aprinted circuit board by the semi additive method.

In the semi-additive method, for example, an insulating layer 11 of aresin film is first prepared, as shown in FIG. 4 (a).

Next, as shown in FIG. 4 (b), a thin conductive film 12 is formed on theinsulating layer 11 by sputtering or electroless plating.

Then, as shown in FIG. 4 (c), a plating resist 13 is formed on the thinconductive film 12 using a dry film resist or the like. The platingresist 13 has patterns opposite to the prescribed patterns of aconductor layer formed in a step shown below.

After this, as shown in FIG. 4 (d), a conductor layer 14 is formed byelectrolytic plating on the surfaces of the thin conductive film 12where the plating resist 13 is not formed.

This is followed by removing the plating resist 13 by, e.g., stripping,as shown in FIG. 4 (e). Then, the thin conductive film 12 except theportions on which the conductor layer 14 is formed is removed bychemical etching or the like, as shown in FIG. 4 (f). In this manner,the conductor layer 14 with prescribed patters is formed on theinsulating layer 11.

However, in the conventional method for forming a printed circuit board,side etching of the thin conductive film 12 under the conductor layer 14may occur during the removal of the thin conductive film 12 except theportions under the conductor layer 14 by chemical etching or the like.The term “side etching” is described now with reference to the figurebelow.

FIG. 5 is a magnified view of the region B in FIG. 4 (f). During theremoval of the thin conductive film 12 by chemical etching or the like,the thin conductive film 12 under the conductor layer 14 was etchedtogether with both ends thereof being gouged as shown in FIG. 5. Thisresults in a deterioration of the adhesion of the conductor layer 14 tothe thin conductive film 12. In the case of a significant decrease inthe adhesion, the conductor layer 14 may be stripped off.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide printed circuitboards that provide improved adhesion of conductor layers and a methodfor manufacturing such printed circuit boards.

A printed circuit board according to one aspect of the inventioncomprises, in sequence, an insulating layer, a thin copper film, and aconductor layer, wherein the conductor layer and the thin copper filmhave prescribed patterns, and the thin copper film has a first surfacein contact with the insulating layer and a second surface in contactwith the conductor layer, and contains a grain of a size that extendsbetween the first surface and the second surface.

In the printed circuit board, the thin copper film and conductor layerwith the prescribed patterns are formed in sequence on the insulatinglayer. The thin copper film contains a grain of a size that extendsbetween the first surface in contact with the insulating layer and thesecond surface in contact with the conductor layer. This reduces orprevents the incidence of side etching of the thin copper film under theconductor layer during the removal of the thin copper film except theportions on which the conductor layer is formed. In this manner, asufficient adhesion area of the thin copper film to the insulating layeris ensured to improve the adhesion.

The thin copper film preferably has a thickness of not less than 50 nmand not more than 300 nm. This further improves the adhesion of theconductor layer to the thin copper film.

The conductor layer may include copper. This even further improves theadhesion of the conductor layer to the thin copper film.

The printed circuit board may further comprise a thin metal film betweenthe insulating layer and the thin copper film. In this manner, asufficient adhesion area of the thin copper film to the thin metal filmis ensured to improve the adhesion.

The thin metal film may include at least one of chromium and nickel.This further improves the adhesion between the insulating layer and thethin copper film.

The thin metal film preferably has a thickness of not less than 5 nm andnot more than 50 nm. This still further improves the adhesion betweenthe insulating layer and the thin copper film.

The insulating layer may include a flexible substrate. The flexiblesubstrate having flexibility allows the flexibility of the printedcircuit board to be improved.

A method for manufacturing a printed circuit board by a semi-additivemethod according to another aspect of the invention comprises the stepsof forming a thin copper film on an insulating layer, forming aconductor layer having prescribed patterns on the thin copper film,removing the thin copper film except portions on which the conductorlayer is formed, and applying a thermal treatment to the thin copperfilm between the step of forming the thin copper film and the step offorming the conductor layer or between the step of forming the conductorlayer and the step of removing the thin copper film.

In the method for manufacturing the printed circuit board, the thincopper film is thermally treated between the step of forming the thincopper film and the step of forming the conductor layer or between thestep of forming the conductor layer and the step of removing the thincopper film, which increases the size of grains contained in the thincopper film. This reduces or prevents the incidence of side etching ofthe thin copper film under the conductor layer during the removal of thethin copper film except the portions on which the conductor layer isformed. Thus, a sufficient adhesion area of the thin copper film to theinsulating layer is ensured to improve the adhesion. In addition, wherea thin metal film is present between the insulating layer and the thincopper film, a sufficient adhesion area of the thin copper film to thethin metal film is ensured to improve the adhesion.

A temperature during the thermal treatment of the thin copper film maybe not less than 200° C. and not more than 300° C. This allows the sizeof grains contained in the thin copper film to be sufficientlyincreased.

The method for manufacturing a printed circuit board may include thesteps of forming a resist on the thin copper film that has patternsopposite to the prescribed patterns, forming a conductor layer on thethin copper film except portions on which the resist is formed, andremoving the resist after forming the conductor layer, and wherein thestep of applying the thermal treatment to the thin copper film isprovided between the step of forming the thin copper film and the stepof forming the resist or between the step of removing the resist and thestep of removing the thin copper film.

In this manner, the step of applying the thermal treatment to the thincopper film is provided between the step of forming the thin copper filmand the step of forming the resist or between the step of removing theresist and the step of removing the thin copper film. This prevents theresist from dissolving by the thermal treatment of the thin copper film.

The manufacturing method may further comprise the step of forming a thinmetal film between the insulating film and the thin copper film. In thismanner, a sufficient adhesion area of the thin copper film to the thinmetal film is ensured to improve the adhesion.

The step of forming the thin metal film may include the step of formingat least one of chromium and nickel as the thin metal film. This furtherimproves the adhesion between the insulating layer and the thin copperfilm.

The step of forming the thin metal film may include the step of formingthe thin metal film having a thickness of not less than 5 nm and notmore than 50 nm. This still further improves the adhesion between theinsulating layer and the thin copper film.

The step of forming the thin copper film on the insulating layer mayinclude the step of forming the thin copper film on a flexible substratethat serves as the insulating layer. The flexible substrate havingflexibility allows the flexibility of the printed circuit board to beimproved.

According to the invention, the thin copper film contains a grain of thesize that extends between the first surface in contact with theinsulating layer and the second surface in contact with the conductorlayer. This reduces or prevents the incidence of side etching of thethin copper film under the conductor layer during the removal of thethin copper film except the portions on which the conductor layer isformed. In this manner, a sufficient adhesion area of the thin copperfilm to the insulating layer is ensured to improve the adhesion. Inaddition, where the thin metal film is present between the insulatinglayer and the thin copper film, a sufficient adhesion area of the thincopper film to the thin metal film is ensured to improve the adhesion.

The foregoing and other objects, features, aspects and advantages of thepresent invention will become more apparent from the following detaileddescription of the present invention when taken in conjunction with theaccompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 (a), 1 (b), 1 (c), and 1 (d) are schematic cross sectional viewsshowing the steps of a method for manufacturing a printed circuit boardaccording to an embodiment of the invention;

FIGS. 2 (e), 2 (f), and 2 (g) are schematic cross sectional viewsshowing the steps of a method for manufacturing a printed circuit boardaccording to an embodiment of the invention;

FIG. 3 is a magnified view of the region A in FIG. 2 (f)

FIGS. 4 (a), 4 (b), 4 (c), 4 (d), 4 (e), and 4 (f) are schematic crosssectional views showing the steps of a method for manufacturing aprinted circuit board by the semi additive method; and

FIG. 5 is a magnified view of the region B in FIG. 4 (f)

DESCRIPTION OF THE PREFERRED EMBODIMENTS

A printed circuit board according to an embodiment of the invention anda method for manufacturing the printed circuit board will be describedbelow with reference to the drawings.

A method for manufacturing a printed circuit board according to anembodiment will be described first. FIGS. 1 (a), 1 (b), 1 (c), and 1 (d)as well as FIGS. 2 (e), 2 (f), and 2 (g) are schematic cross sectionalviews showing the steps of a method for manufacturing a printed circuitboard according to an embodiment of the invention.

To begin with, as shown in FIG. 1 (a), an insulating layer 1 made of,e.g., an insulator film, is prepared. Such an insulator film is made ofpolyimide or polyester, for example. Alternatively, the insulating layer1 may be formed by applying a resin onto a substrate made of a metalfoil.

Next, a thin metal film 2 and a thin copper film 3 are formed insequence on the insulating layer 1, as shown in FIG. 1 (b). The thinmetal film 2, which is provided to improve the adhesion between theinsulating layer 1 and the thin copper film 3, may only be provided whennecessary. Each of the thin metal film 2 and thin copper film 3 isformed by sputtering, electroless plating, or other suitable means.

The thin metal film 2 as used here includes at least either of chromiumand nickel. For example, the thin metal film 2 may be made of a singlelayer of chromium, a laminated film of chromium and nickel, or a film ofa chromium-nickel alloy. The thickness of the thin metal film 2 ispreferably in the range of not less than 5 nm and not more than 50 nm,for example. This further improves the adhesion of the thin copper film3 to the insulating layer 1.

The thickness of the thin copper film 3 is preferably in the range ofnot less than 50 nm and not more than 300 nm, for example. This furtherimproves the adhesion of conductor patterns 5 described below to thethin copper film 3.

Then, as shown in FIG. 1 (c), the thin copper film 3 is laminated with,e.g., a dry film, and exposed and developed to form plating resist 4thereon. The plating resist 4 have patterns opposite to the conductorpatterns 5 which are formed in a step shown below.

After this, as shown in FIG. 1 (d), the conductor patterns 5 are formedon the surfaces of the thin copper film 3 where the plating resist 4 isnot formed by electrolytic plating using, e.g., a copper sulfateelectrolytic plating solution. A metal or an alloy other than copper mayalso be used as the material of the conductor patterns 5.

The plating resist 4 is subsequently removed by, for example, stripping,as shown in FIG. 2 (e). Then, a thermal treatment is applied to the thincopper film 3. During the thermal treatment, the thin copper film 3 isheld at a temperature of not less than 200° C. and not more then 300°for approximately an hour, preferably not less than half an hour and notmore than two hours. Setting the time to not less than half an hour andnot more than two hours as described above allows the grain size to besufficiently increased while preventing consumption of an excessiveenergy.

The above-described thermal treatment allows the grain size of the thincopper film 3 to be increased. For example, in this embodiment, thegrain size of the thin copper film 3 is as large as approximately notless than 40 nm and not more than 300 nm.

After this, as shown in FIG. 2 (f), the thin copper film 3 and thinmetal film 2 are removed, by chemical etching using, e.g., a mixedsolution of a sulfuric acid and oxygenated water, except the portions onwhich the conductor patterns 5 are formed.

Then, as shown in FIG. 2 (g), a protective insulating layer 6 ofpolyimide or the like having prescribed patterns is formed. In thiscase, a terminal is provided on the portion of each conductor pattern 5that is not covered with the protective insulating layer 6 (i.e., anaperture).

Note that the above-described thermal treatment is possible without aplating resist being formed. For example, the thermal treatment may beperformed between the step of FIG. 1 (b) and the step of FIG. 1 (c).

Now, advantageous effects provided by the above-described thermaltreatment of the thin copper film 3 will be described.

FIG. 3 is a magnified view of the region A in FIG. 2 (f). As shown inFIG. 3, thermally treating the thin copper layer 3 allows the size ofgrains contained in the thin copper layer 3 to be increased.

That is, in this embodiment, the thermally treated thin copper film 3contains a grain 21 of such size as to extend between one surface of thethin copper film 3 in contact with the insulating layer 1 and the othersurface of the thin copper film 3 in contact with the conductor pattern5. That is, the thin copper film 3 has a point where only a single grain21 is present in the thickness direction V. This reduces or prevents theincidence of side etching of the thin copper film 3 under the conductorpattern 5 during the removal of the thin copper film 3 except theportion on which the conductor pattern 5 is formed. This ensures asufficient adhesion area of the thin copper film 3 to the insulatinglayer 1 to improve the adhesion. Where the thin metal film 2 is presentbetween the insulating layer 1 and the thin copper film 3, a sufficientadhesion area of the thin copper film 2 to the thin metal film 2 isensured to improve the adhesion.

Although in this embodiment, the use of polyimide, polyester, or thelike as the material of the insulating layer 1 is described, any otherhighly insulating films of plastics may also be used as the insulatinglayer 1. For example, a polyethylene terephthalate film, a polyethylenenaphthalate film, a polyether nitril film, polyethersulfone film, apolyvinyl chloride film or the like may be used.

It is preferred to use, in particular, a polyimide film, a polyethyleneterephthalate film, or a polyethylene naphthalate film, since they aresuperior in such properties as thermal resistance, dimensionalstability, electrical properties, mechanical properties, and chemicalresistant properties.

EXAMPLES Inventive Example

A printed circuit board according to Inventive Example and the methodfor manufacturing the printed circuit board will be described below. Themanufacturing method according to Inventive Example is based upon themanufacturing method according to the above-described embodiment, andtherefore the description of drawings is omitted.

First, an insulating layer 1 made of a 25-μm polyimide insulator filmwas prepared.

Next, a thin metal film 2 made of 30-nm nichrome and a 200-nm thincopper film 3 were formed in sequence on the insulating layer 1 bysputtering.

Then, the thin copper film 3 was laminated with a dry film, and thenexposed and developed to form a plating resist 4 thereon having patternsopposite to conductor patterns that are formed in a step shown below.

After this, conductor patterns 5 of copper with a thickness of 8 μm, awidth of 15 μm, and a pitch of 15 μm were formed, by electrolyticplating using a copper sulfate electrolytic plating solution, on thesurfaces of the thin copper film 3 where the plating resist 4 was notformed.

The plating resist 4 was then stripped off, after which the thin copperfilm 3 was held at 250° C. for an hour to be thermally treated.

Then, the thin copper film 3 and thin metal film 2 were removed exceptthe portions under the conductor patterns 5 by chemical etching using amixed solution of a sulfuric acid/oxygenated water. This was followed bythe formation of a protective insulating film 6 of polyimide havingprescribed patterns.

A cross section of thus fabricated printed circuit board was observedwith a scanning electron microscope (SEM).

The results showed that the thin copper film 3 contained grains of thesize equal to the thickness of the thin copper film 3, 200 nm; i.e.,grains of such size as to extend between one surface of the thin copperfilm 3 in contact with the thin metal film 2 and the other surface ofthe thin copper film 3 in contact with the conductor patterns 5 in thethickness direction V.

In addition, the thin copper film 3 under the conductor patterns 5 didnot show any side etching.

Stripping tests using an adhesive tape were also conducted in order tocheck the conductor patterns 5 for adhesion to the thin copper film 3.The results confirmed that the conductor patterns 5 were not stripped atall, and possessed good adhesion.

Comparative Example

The method for manufacturing a printed circuit board according toComparative Example differed from the above-described method accordingto Inventive Example in that the thin copper film 3 was not thermallytreated.

After the fabrication of the printed circuit board, a cross section ofthe printed circuit board was observed with SEM, as in theabove-described Inventive Example.

The results showed that the sizes of all of grains contained in the thincopper film 3 were less than 200 nm, and there always existed two ormore grains between one surface of the thin copper film 3 in contactwith the thin metal film 2 and the other surface of the thin copper film3 in contact with the conductor patterns 5 in the thickness direction V.

Further, the thin copper film 3 under the conductor patterns 5 showedside etching.

Stripping tests using an adhesive tape were also conducted in order tocheck the conductor patterns 5 for adhesion to the thin copper film 3.The results confirmed that part of the conductor patterns 5 was strippedoff, and did not possess good adhesion.

Although the present invention has been described and illustrated indetail, it is clearly understood that the same is by way of illustrationand example only and is not to be taken by way of limitation, the spiritand scope of the present invention being limited only by the terms ofthe appended claims.

1. A printed circuit board comprising, in sequence, an insulating layer,a thin copper film, and a conductor layer, wherein said conductor layerand said thin copper film have prescribed patterns, and said thin copperfilm has a first surface in contact with said insulating layer and asecond surface in contact with said conductor layer, and contains agrain of a size that extends between said first surface and said secondsurface.
 2. The printed circuit board according to claim 1, wherein saidthin copper film has a thickness of not less than 50 nm and not morethan 300 nm.
 3. The printed circuit board according to claim 1, whereinsaid conductor layer includes copper.
 4. The printed circuit boardaccording to claim 1, further comprising a thin metal film between saidinsulating layer and said thin copper film.
 5. The printed circuit boardaccording to claim 4, wherein said thin metal film includes at least oneof chromium and nickel.
 6. The printed circuit board according to claim4, wherein said thin metal film has a thickness of not less than 5 nmand not more than 50 nm.
 7. The printed circuit board according to claim1, wherein said insulating layer includes a flexible substrate.
 8. Amethod for manufacturing a printed circuit board by a semi-additivemethod, comprising the steps of: forming a thin copper film on aninsulating layer; forming a conductor layer having prescribed patternson said thin copper film; removing said thin copper film except portionson which said conductor layer is formed; and applying a thermaltreatment to said thin copper film between said step of forming saidthin copper film and said step of forming said conductor layer orbetween said step of forming said conductor layer and said step ofremoving said thin copper film.
 9. The method for manufacturing aprinted circuit board according to claim 8, wherein a temperature duringsaid thermal treatment of said thin copper film is not less than 200° C.and not more than 300° C.
 10. The method for manufacturing a printedcircuit board according to claim 8, wherein said step of forming saidconductor layer includes the steps of: forming a resist on said thincopper film that has patterns opposite to said prescribed patterns;forming a conductor layer on said thin copper film except portions onwhich said resist is formed; and removing said resist after forming saidconductor layer, and wherein said step of applying said thermaltreatment to said thin copper film is provided between said step offorming said thin copper film and said step of forming said resist orbetween said step of removing said resist and said step of removing saidthin copper film.
 11. The method for manufacturing a printed circuitboard according to claim 8, further comprising the step of forming athin metal film between said insulating film and said thin copper film.12. The method for manufacturing a printed circuit board according toclaim 11, wherein said step of forming said thin metal film includes thestep of forming at least one of chromium and nickel as said thin metalfilm.
 13. The method for manufacturing a printed circuit board accordingto claim 11, wherein said step of forming said thin metal film includesthe step of forming said thin metal film having a thickness of not lessthan 5 nm and not more than 50 nm.
 14. The method for manufacturing aprinted circuit board according to claim 8, wherein said step of formingsaid thin copper film on said insulating layer includes the step offorming said thin copper film on a flexible substrate that serves assaid insulating layer.